| 產(chǎn)品中心 >> Automotive Electronics Industry >> a.Designed as an encapsulation material for dry Ignition coil of the car or the other transformer, electronic igniter |
|
| 產(chǎn) 品 類(lèi) 別 |
| Epoxy potting resin material for dry Ignition coil of the car
|
|
| 產(chǎn) 品 特 點(diǎn) |
| High Tg, good cracking resistance, good impact resistance, good immersion
|
|
| 應(yīng) 用 范 圍 |
| Designed as an encapsulation material for dry Ignition coil of the car or the other transformer, electronic igniter
|
|
| 產(chǎn) 品 性 能 |
6100A/B-2BE
|
Properties
|
Test Conditions
|
Unit
|
Index
|
|
Component A
|
-
|
-
|
6100A-2BE
|
|
Component B
|
-
|
-
|
6100B-2BE
|
|
Component A viscosity
|
40℃
|
mPa·s
|
10000～30000
|
|
Component B viscosity
|
40℃
|
mPa·s
|
15～25
|
|
Component A specific gravity
|
25℃
|
g/cm3
|
1.70±0.03
|
|
Component B specific gravity
|
25℃
|
g/cm3
|
1.20±0.02
|
|
Proportion(A/B)
|
by weight
|
-
|
100：28
|
|
Curing
conditions
|
-
|
-
|
85℃/4hr + 105℃/1hr + 125℃/2.5hr
|
|
Hardness
|
25℃
|
Shore
D
|
≥88
|
|
Inflecting strength
|
-
|
MPa
|
≥65
|
|
Glass transition temperature
|
DSC，10℃/min
|
℃
|
85～95
|
|
Coefficient of thermal expansion a1
|
TMA，0-30℃
|
K-1
|
≤6.7×10-5
|
|
Water absorption
|
100℃/30min
|
%
|
≤0.15
|
|
Cure shrinkage rate
|
Solid
liquid density ratio
|
%
|
≤2.5
|
|
K1C
|
-
|
MPa.m1/2
|
≥2.0
|
|
GIC
|
-
|
KJ/m2
|
≥0.7
|
|
Volume resistance
|
Normal
|
Ω·m
|
≥1.0×1013
|
|
Dielectric constant
|
1MHz，25℃
|
-
|
4.2±0.3
|
|
Dissipation factor
|
1MHz，25℃
|
%
|
≤1.50
|
|
Electric strength
|
Normal
|
MV/m
|
≥20.0
|
|
|
|