| 產(chǎn)品中心 >> Automotive Electronics Industry >> e.Designed as an epoxy potting resin material for pen Ignition coil of the car or the other transformer, electronic igniter |
|
| 產(chǎn) 品 類 別 |
| Epoxy potting resin material for pen Ignition coil of the car
|
|
| 產(chǎn) 品 特 點 |
| Good insulation, high Tg, good cracking resistance, good impact resistance, good immersion
|
|
| 應(yīng) 用 范 圍 |
| Designed as an epoxy potting resin material for pen Ignition coil of the car or the other transformer, electronic igniter.
|
|
| 產(chǎn) 品 性 能 |
6103A /B -J03
|
Properties
|
Test Conditions
|
Unit
|
Index
|
|
Component A
|
-
|
-
|
6103A-J03
|
|
Component B
|
-
|
-
|
6103B-J03
|
|
Component A viscosity
|
90℃
|
mPa·s
|
6000~16000
|
|
Component B viscosity
|
40℃
|
mPa·s
|
20～40
|
|
Component A specific gravity
|
25℃
|
g/cm3
|
1.70±0.03
|
|
Component B specific gravity
|
25℃
|
g/cm3
|
1.16±0.02
|
|
Proportion(A/B)
|
by weight
|
-
|
100：28
|
|
Curing
conditions
|
-
|
-
|
100℃/3hr + 150℃/3hr（oven）
75℃/120min+75℃→145℃/120min+145℃/180min
|
|
Hardness
|
25℃
|
Shore
D
|
≥90
|
|
Inflecting strength
|
25℃
|
MPa
|
≥140
|
|
Inflecting modulus
|
25℃
|
MPa
|
6500～7500
|
|
Glass transition temperature
|
DSC，10℃/min
|
℃
|
≥140
|
|
Coefficient of thermal
expansion a1
|
TMA，10℃/min
|
ppm/K
|
≤40
|
|
Coefficient of thermal
expansion a2
|
TMA，10℃/min
|
ppm/K
|
≤140
|
|
Water absorption
|
100℃/30min
|
%
|
≤0.1
|
|
Volume resistance
|
500V，25℃
|
Ω·m
|
≥1.0×1014
|
|
Dielectric constant
|
1MHz，25℃
|
-
|
4.2±0.3
|
|
Dissipation factor
|
1MHz，25℃
|
%
|
≤1.5
|
|
Electric strength
|
25℃
|
MV/m
|
≥23.0
|
|
|
|