| 產品中心 >> Electrical Industry >> Used for potting αnd insulation of various electrical, high voltage electronic αnd electrical devices |
|
| 產 品 類 別 |
| Thermal and flame Retardant Epoxy Resin Compounds for Potting
|
|
| 產 品 特 點 |
| Excellent high and low temperature impact property, high Tg , environmental product, flame retardant, good electrical and mechanical property
|
|
| 應 用 范 圍 |
| Used for potting and insulation of various electrical, high voltage electronic and electrical devices
|
|
| 產 品 性 能 |
5201A/B-23B Series
|
Properties
|
Test Conditions
|
Unit
|
Index
|
|
Component A
|
-
|
-
|
5201A-23B,5201A-23BE
|
|
Component B
|
-
|
-
|
5201B-23
|
|
Component A viscosity
|
40℃
|
mPa·s
|
1500～3000
|
|
Component B viscosity
|
40℃
|
mPa·s
|
5～15
|
|
Component A specific gravity
|
25℃
|
g/cm3
|
1.70±0.03
|
|
Component B specific gravity
|
25℃
|
g/cm3
|
0.96±0.03
|
|
Proportion(A/B)
|
by weight
|
-
|
100：10-13
|
|
Curing
conditions
|
-
|
-
|
80℃/3h or 25℃/24h
|
|
Hardness
|
（Shore D）
|
25℃
|
83-90
|
|
Inflecting strength
|
25℃
|
MPa
|
≥60
|
|
Inflecting
modulus
|
25℃
|
MPa
|
5000-8000
|
|
Glass transition temperature
|
DSC,10℃/min
|
℃
|
≥80
|
|
Coefficient of thermal expansion a1
|
TMA,10℃/min
|
ppm/℃
|
45-55
|
|
Coefficient of thermal
expansion a2
|
TMA,10℃/min
|
ppm/℃
|
140-180
|
|
Thermal conductivity
|
Hot-wire
technique
|
W/m.K
|
≥0.75
|
|
Water absorption
|
100℃/30min
|
%
|
≤0.3
|
|
Volume resistance
|
Normal
|
Ω·m
|
≥1.0×1010
|
|
Dielectric constant
|
1MHz，25℃
|
-
|
5.1-5.7
|
|
Dissipation factor
|
1MHz，25℃
|
%
|
0.5-1.0
|
|
Electric strength
|
Normal
|
MV/m
|
≥18.0
|
|
Flammation Preventable（6.0mm）
|
（UL94）
|
-
|
V-0
|
|
|
|